Heat Shrinkable Wraparound Jacket Repair Sleeve

DESCRIPTIONS

Compaq heat shrink wraparound sleeves are manufactured from thermally stabilized cross-linked polyolefin, with a hot melt adhesive liner on the inner side of the sleeves. Upon heating, the sleeve shrinks and the adhesive melts, creating a water tight bond between the sleeve and cable sheath or cable Joint assembly components. CRS wraparound sleeve meat & even exceed the various national & international quality standards applicable. A corrosion proof stainless steel channel is used to close the sleeve during installation.
Compaq heat shrinkable wraparound sleeves are designed to repair damaged cable sheath. It is also suitable for use for rejecting of cable Joints and as additional corrosion protection on undamaged cables.
Quick & easy to apply, it provides maximum protection against correction & waterproof.

DESCRIPTIONS

  • Provides water tight seal upon recovery
  • Excellent mechanical strength
  • Application procedure is quick, simple & clean
  • Covered with thermochromatic paint that change colure upon achieving correct shrink temperature
  • Sleeve can be cut to suit shorter application requirement on site.
  • Stainless steel channel provides permanent closer system

SELECTION GUIDE

Product Code Expended I.D.
(Min) D1
Recovered I.D.
(Max)D2
Application Range (Dia) (mm) Recovered Wall
Thickness (W)
CRS-42/8 52 8 15-35 2.7
CRS-53/13 53 13 20-45 2.7
CRS-62/22 62 22 30-50 2.7
CRS-92/30 92 30 37-70 2.7
CRS-122/38 122 38 48-100 2.7
CRS-140/45 140 45 55-125 2.7
CRS-160/50 160 50 65-140 2.7
CRS-210/60 210 60 72-160 2.7

D 1 - Dimensions as supplied • D 2 - Dimension after full shrinking • W - Wall thickness after full recovery

TECHNICAL SPECIFICATIONS

Properties Value Standard
Physical    
Tensile Strength 17 n/mm2 (Mpa)(Min) ASTM D638/ISO 37
Ultimate Elogation 300 % (Min) ASTM D 638/ISO 37
Longitudinal Change 10 % (Min) ASTM D 2671
Water Absorption 0.2% (Max) ASTM D570/ISO 62
ESCR 48 hrs. for 500C No Crack ASTM D570
Torchability No Split TE 201 AOL
Accelerated Ageing (1200C for 500 hrs ASTM D2671/ISO 188
Tensil Strength 15 N/mm2 (Mpa) (Min) ASTM D638
Ultimate Elongation 220% (Min) ASTM D638
Low Temperature Flexibility
4 Hours at 200 C + 30C
No Cracking ASTM 2671
Temp. Including Paint Conversion
1500C for 30 min
2500C for 5 min
No change
Colour Change
Visula
Visula
Electrical    
Dielectric Strength 12 kV/mm ASTM D149/IEC 60243
Volume Resistivity 1 x 1012 ohm cm Min IEC 60093
Dielectric Constant 5 Max IEC 60250
Chemical    
Chemical Resistance in 0.1 N    
Sol. of Na2So4Na2NaCI2H2So4    
Tensil Strength 15 N/mm2 (Mpa) (Min) ASTM D6328/ISO 37
Elogation 200% (Min) ASTM D638/ISO 37